Resutop FH is a fast curing, two-pack, high-build epoxy coating for application as a chemical resistant heavy-duty floor coating for temperatures from 30°C down to 5°C. The coating will provide a smooth gloss finish to which anti-slip aggregate can be added if required. Applied by squeegee, roller and paintbrush the product is low odour producing a seamless, hard wearing, hygienic floor finish allowing a faster return to service.
New concrete must be clean, sound, dry, fully cured and surface laitance removed by vacuum enclosed shot blasting or mechanical grinding, a minimum strength of 25N/mm² is required.
Existing Concrete Floors:
Remove all dirt, oil, grease, old paint or any other surface contaminants by vacuum enclosed shot blasting, scarifying or mechanical grinding. Fats, oils or greases must be removed by mechanical means and detergent washing and making sure all residue of detergent is washed and removed by rinsing with clean water. Local repairs should be carried out using Resuscreed PA.
All previous coatings and loose floor paints must be removed by mechanical preparation as described in the above section and primed as specified. If the old resin flooring cannot be removed then please consult with our technical team for advice on intercoat adhesion and suitability, as it may not be compatible with the existing floor coating.
Where Resutop FH is applied to masonry/concrete surfaces, care must be taken to ensure that surface preparation is thorough but does not disfigure the surface.
Mixing: Mix the entire contents of the base with the hardener.
If a separate mixing bucket is being used mix thoroughly ensuring all contents of both components are removed from the buckets supplied. Mix using a slow speed electric mixer for approximately two to three minutes until the two components are fully combined.
The mixed unit should be applied immediately by roller, brush or squeegee with a consistent procedure. Floor areas should be cross-rolled to ensure even application and to minimise roller marks.
The ambient temperatures of the areas should not be allowed to fall below 15°C throughout the application and the curing period, as this could have an adverse effect on the appearance and colour of the system. The surface temperature must be above 5°C. Where possible it is recommended that the application area is heated to a minimum temperature of 15°C ideally to allow the ambient and substrate temperature to stabilise prior to the installation.
NOTE: Applied coating should be protected from moisture during application and during the curing period. Exposure to moisture during this time can cause surface and colour variations.
Full product data sheets and safety data sheets are available on request.
Volume Solids: ~100%
VOC: Colours: Black, Buff, Flint, Salsa, Stirling, White, Forest, Kingfisher, Tuscan Glade
Finish: Smooth gloss
Flash Point: N/A
Pack Size: 5 kg
Mixing Ratio: 4 parts base to 1 part hardener by weight Only
Pack Weights: 4kg base/1kg hardener (5kg)
Mixed Density: Approximately 1.30 g/cm3
Shelf Life: 36 months (Base) & 24 Months (Hardener)
Storage: Keep out of direct sunlight. Store in a dry place, between 15°C – 30°C
Recommended Application Methods:
Brush, roller or squeegee
Application at 20°C
Recoating Intervals: 3-4 hours or once the surface has lost tackiness at 20oC, 18 hours at 5oC
Light Traffic: 8 – 12 hours, 18 hours at 5°C
Full Traffic: 16 – 24 hours, 48 - 72 hours at 5°C
Full Chemical Cure 7–10 days
Pot Life: 15 – 20 minutes from mixing, based on 5 kg pack size
The pot life may be shorter for larger pack sizes if the paint is not used within the pot life limit.
Note: All mixed paint must be used within the pot lifetime limit, if the paint is left in the container after mixing and not used, it may release hazardous fumes due to exothermic reaction.
Coverage Rate: 5 kg will cover 19m² @ 200 µm
Coverage rate is calculated based on a sealed and smooth surface and may vary based on the substrate roughness and other conditions.
System Thickness: 200 – 250 µm
The suggested thickness range is calculated based on average volume solid as a general recommendation for the specified condition and for each application may vary
FeRFA Category: Category 2
(ASTM D4060) 83.9mg loss per 1000 cycles
(BS EN ISO 527-2:2012) 20 N/mm2
(BS EN 13892-8:2002) >3 N/mm2 (Substrate failure)
(BS EN 1504-2:2004) Class I
Reaction to Fire:
(EN 13501-1:2018) Bfl-s1
Temperature Resistance: Tolerant of temperatures up to 60°c
Chemical Resistance: Good